Zheflon®FL2604 PVDF- Squeeze Grade

Group	PVDF for others
Min. Order	1 piece
Terms of Payment	all
Update Time	2019-06-14

Item specifics

Features	Copolymer. Medium viscosity
Uses	Optical fiber. Hose
Forms	White powder or translucent particles

Description
Product review

PVDF Characteristic

Process safety instructions

Packaging and storage

Zheflon® FL2604 is a medium viscosity grade polyvinylidene fluoride copolymer with high purity. Important properties include excellent chemical resistance to most aggressive substances and solvents, excellent mechanical strength and toughness, high abrasion resistance, high temperature capabilities, excellent aging resistance, low permeability to most gases and liquids and easily melt-processed by standard methods of squeeze. Also can be used for the production of lithium battery separators.

General
Features	Copolymer. Medium viscosity
Uses	Optical fiber. Hose
Forms	White powder or translucent particles
Items	Typical Value FL2604	Test Method
Physical Properties
Density（g/cc）	1.76~1.79	ASTM D792
Melt Flow Rate（g/10min）	2.0~6.0	Load 12.5kg，230℃，ASTM D1238
Melt viscosity（Kps）	20~25	Shear Rate 100 1/s，ASTM D3835
Water Absorption（%）（Time 24 hr）	≤0.010	ISO 62
Molecular Properties
Molecular weight（Da）	400,000~480,000	GPC,DMF,ISO 16014
Intrinsic viscosity（dl/g）	1.20~1.40	30℃,DMAC
Molecular weight distribution	1.8-2.3	GPC,DMF,ISO 16014
Mechanical Properties
Tensile Modulus（Thickness2.00mm）（MPa）	500~900	1.0mm/min,ASTM D638
Flexural Modulus（Thickness2.00mm）（MPa）	600~900	2.0mm/min,ASTM D790
Yield Strength（Thickness2.00mm）（MPa）	30.0~45.0	50mm/min,ASTM D638
Break Strength（Thickness2.00mm）（MPa）	20.0~30.0	50mm/min,ASTM D638
Elongation at Yield（%）	10.0~20	50mm/min,ASTM D638
Elongation at Break（%）	200~400	50mm/min,ASTM D638
Hardness, Shore D（Thickness2.00mm）	65~70	ASTM D2240
Thermal Properties
Melting Point（℃）	140~145	ASTM D3418
Glass Transition Temp, Tg（℃）	-42.0~39	ASTM E1356
Decomposition Temperature（℃）	375	1% wt. loss / in air

1.PVDF should be processed under 260℃,to avoid producing toxic gases；

2.PVDF has good fire resistance and smoke inhibition property, however, when meets with fire, it will release toxic hydrogen fluoride gas and fluorocarbon compounds；

3.Operators should take good care of personal protection during the use procedure and processing.

PVDF is packed in PE plastic bag and then be put into a drum with the net weight 25KGS. It must be stored in clean, cool, dry place.